These three extrusion methods are based on the difference in the moisture content of the molding.When the moisture content more than 16%,wet billet molding is plastic extrusion molding. When the moisture content equals 14-16%, it’s semi-hard plastic extrusion molding. When the moisture content equals 12-14% ,it’s hard plastic extrusion molding.Blank forming includes: feeding material , mixing,adding water and grinding equipment processing before raw materials entering the molding shop not brick extruding machine.After passing through the molding brick machine, the qualified mud and wet billet are formed.Forming process should fulfill the requirement of the shape and structure.Forming is the foundation of the brick making process.The quality of the formed body is directly related to the appearance quality of the finished tile.

After the wet billets formed from the molding plant, they need to be dried by dehydration.In the production process of sintered bricks, there are two ways of drying wet blank: natural drying and artificial drying.

Automatic Cement Brick Making Machine For Bangladesh/Brick Machine Making 4-20

 b, Another reason for resulting in failure of the vacuum chamber, is the sand-based raw material, so the closed mud layer of the upper auger is too thin, easy to be drawn through, causing the vacuum failure, so the adobe could not be molded. The best way to solve this problem is to change the ratio of raw materials, to increase the plasticity index of raw materials. The other way is to cut the front end of the superiors auger to 2-10 centimeters according to the material properties of soil (must be conducted under the guidance of skilled technical personnel, don’t do it by yourself).

Automatic Cement Brick Making Machine For Bangladesh/Brick Machine Making 4-20

5, Many brick cracks on adobes or broke into two sections, more wastes after sintering.

Reasons: There are too many viscous ingredients in raw materials, so the plasticity index is too high.

Solutions: change the ratio of raw materials, reduce the plasticity index. The plasticity index of clay can be up to 25, can be properly incorporated into the coal ash, slag, fly ash or waste of brick powder to make it thin.