These three extrusion methods are based on the difference in the moisture content of the molding.When the moisture content more than 16%,wet billet molding is plastic extrusion molding. When the moisture content equals 14-16%, it’s semi-hard plastic extrusion molding. When the moisture content equals 12-14% ,it’s hard plastic extrusion molding.Blank forming includes: feeding material , mixing,adding water and grinding equipment processing before raw materials entering the molding shop not brick extruding machine.After passing through the molding brick machine, the qualified mud and wet billet are formed.Forming process should fulfill the requirement of the shape and structure.Forming is the foundation of the brick making process.The quality of the formed body is directly related to the appearance quality of the finished tile.

After the wet billets formed from the molding plant, they need to be dried by dehydration.In the production process of sintered bricks, there are two ways of drying wet blank: natural drying and artificial drying.

Qt40-2 Manual Brick Making Machine Concrete Interlocking Bricks Making Machine Nepal

why clay brick break, why clay brick crack ,why does brick crack?

Most of brick factory owners spent a lot of time and fianace to start their brick factories, however,not all of them get success, the reasons is that before starting clay brick factory, they did not conduct enough study and servey. To avoid investment loss for clay brick production, we have made the following summary for the common phenomenon of poor quality bricks and common mistakes the new clay brick facotry owners always make.

Qt40-2 Manual Brick Making Machine Concrete Interlocking Bricks Making Machine Nepal

1, Malformed adobe, appears large cracks. In more serious cases, the whole adobe will split.

Reasons: the plasticity index of pug is too low, almost no plasticity.

Solution: to increase the plasticity index of raw materials, such as clay, coal slime or clay agent, etc.

For raw materials of low plasticity index, it can also be improved after aging, watering, stirring, rolling, extruding and other methods.